Hshieh, F. Y.
|
Williams, J. H.
- Title
- Further Study of Factors Affecting Pneumatic-Impact Ignition of Polymers.
- Coporate
- NASA Johnson Space Center White Sands Test Facility, Las Cruces, NM
- Journal
-
Fire and Materials,
Vol. 30,
No. 6,
425-437,
November/December 2006
- Keywords
-
polymers
|
ignition
|
plastics
|
impact
|
heating
|
oxygen concentration
|
test methods
|
chemical composition
|
autoignition temperature
- Identifiers
- threshold oxygen concentration; description of materials; Shore D hardness and autoignition temperature of plastics; ignition probability of polymers (impacted in 100% O2 at 20.7 MPa); ignition probability of PEEK (polyetheretherketone) in oxygen concentrations at 20.7 MPa; ignition probability of Teflon PTFE (polytetrafluoroethylene) in oxygen concentrations at 20.7 MPa; ignition probability of Neoflon CTFE (polychlorotrifluoroethylene) in oxygen concentrations at 20.7 MPa; ignition probability of Buna N (acrylonitrile butadiene rubber) in oxygen concentrations at 20.7 MPa; ignition probability of Viton A (copolymer of vinylidene fluoride and hexafluoropropylene) in oxygen concentrations at 20.7 MPa; ignition probability of Zytel 42 (nylon 6/6) in 21% oxygen at 20.7 MPa